EN 10025-2 High strength S235JR Hot rolled steel coil
S235JR Hot rolled steel coil is a low carbon, high tensile strength structural steel which can be readily welded to other weldable steel. EN 10025-2 High strength S235JR Hot rolled steel coil with its low carbon equivalent, it possesses good cold-forming properties.
Grade
|
C%
|
Si %
|
Mn %
|
P %
|
S %
|
N %
|
Cu %
|
S235JR
|
0.23
|
–
|
1.50
|
0.045
|
0.045
|
0.014
|
0.60
|
EN 10025-2 S235JR Mechanical Property:
Grade
|
Thickness
(mm) |
Min Yield
(Mpa) |
Tensile
(Mpa) |
Elongation
(%) |
Min Impact Energy
| |
S235JR
|
8mm-100mm
|
215Mpa-235Mpa
|
360-510Mpa
|
24-26%
|
20
|
27J
|
101mm-200mm
|
185-195Mpa
|
350-490Mpa
|
22%
|
20
|
27J
| |
201mm-400mm
|
–
|
–
|
21%
|
20
|
27J
| |
The min impact energy is longitudinal energy
| ||||||
Because of the low Carbon content and without alloy element, EN 10025-2 High strength S235JR Hot rolled steel coil has the proper tensile strength, good toughness, plasticity, processing property.